Non-Asbestos Jointing Sheets
The non-asbestos jointing sheets made of special non-asbestos heat-resisting Fibre, heat-resisting packing material and nature rubber compound heating and compression molding it. The non-asbestos jointing sheets can Substitution of corresponding models of asbestos rubber sheet, used for the equipment in water,steam,etc.and used as sealing material in the joints of pipeline.
Model:KXT ARS
Send Inquiry
Product Description
Material: Non-Asbestos Jointing Sheets Made of special non-asbestos heat-resisting Fibre, heat-resisting packing material and nature rubber compound heating and compression molding it.
Uses: Substitution of corresponding models of asbestos rubber sheet ,Used for the equipment in water,steam,etc.and used as sealing material in the joints of pipeline
Working pressure : 1.5 MPa ,Working temperature : 20
Sizes:
4100 x 1500 x (0.5 - 6.0)mm, 2000 x 1500 x (0.5 - 6.0)mm,
1500 x 1360 x (0.5 - 6.0)mm, 3810 x 1270 x (0.5 - 6.0)mm
1270 x 1270 x (0.5 - 6.0)mm, 1500 x 1500 x (0.5 - 6.0)mm
The other size is optional or according to the requirements of customers.
| Item | KNXB200 | KNXB300 | KNXB350 | KNNY150 | KNNY250 | KNNY300 | KNNY350 |
| Tensile strength MPa | 5.0 | 7.0 | 11.0 | 8.0 | 10.0 | 12.0 | 15.0 |
| Aging Coefficient | 0.9 | ||||||
| Density g/cm³ | 1.6 - 2.0 | 1.6 - 1.8 | |||||
| Compressibility % | 12 7 | ||||||
| Rebound degree | 35 | 40 | 45 | 40 | 45 | 50 | 50 |
| Pliability | No Crack | ||||||
| Stress-relaxation | 45 | 45 | 45 | 40 | 40 | 30 | 30 |
| Oil sealing With the temperature of 15to 30,.75#aviation gasoline for 30 min |
|
|
|
10 MPa pressure for 30 min No leaking | 12 MPa pressure for 30 min No leaking | 15MPa pressure for 30 min No leaking | 16 MPa pressure for 30 min No leaking |
| With the temperature of 1502,dipped in No.20 aviation oil for 5h,then taken out and laid for 5min. | Tensile strength-reducing % | 40 | 30 | 25 | 25 | ||
| Thickness-increasing % | 5-20 | 5-20 | 5-18 | 5-18 | |||
| Appearance change | No bubble | ||||||
| With the temperature of 15 to 30 ,dipped in No.75 aviation oil for 5h,then taken out and laid for 5min. | Tensile strength MPa | 5 | 6 | 8 | 10 | ||
| Thickness-increasing % | 5-25 | 5-25 | 5-20 | 5-20 | |||
| Pliability | No Crack | ||||||